ASTM A 199 gelegeerde stalen buizen met warmtewisselaar
Oct 27, 2023
materiaalvergelijking vanASTM A 199 warmtewisselaarbuis
|
ASTM-standaard |
Japans |
Duits |
Brits |
||
|
JIS-nr |
DIN-type |
DIN-nr |
BS-nr |
BS-klasse |
|
|
A199 T5 |
STBA25 |
12 crmo19 5 |
3606 |
CFS625 |
|
|
A199 T11 |
STBA23 |
DIN17175 |
13crmo44 |
3606 |
CFS621 |
|
A199 T22 |
STBA24 |
SEW610 |
10 crmo9 10 |
3606 |
CFS622 |
|
A199 t9 |
STBA26 |
DIN17175 |
12CrMo195 |
3606 |
|
Chemische analyse van ASTM A199 (%):
|
Staalkwaliteit |
C |
Mn |
P (maximaal) |
S (maximaal) |
Si |
Cr |
ma |
|
ASTM A199 T4 |
0.15MAX |
0.30-0.60 |
0.03 |
0.03 |
0.50-1.0 |
2.15-2.85 |
0.44-0.65 |
|
ASTM A199 T5 |
0.50-0.15 |
0.30-0.60 |
0.03 |
0.03 |
0.50MAX |
4.00-6.00 |
0.45-0.65 |
|
ASTM A199 T9 |
0.15MAX |
0.30-0.60 |
0.03 |
0.03 |
0.25-1.0 |
8.00-10.0 |
0.90-1.10 |
|
ASTM A199 T11 |
0.50-0.15 |
0.30-0.60 |
0.03 |
0.03 |
0.50-1.0 |
1.00-1.50 |
0.44-0.65 |
|
ASTM A199T22 |
0.50-0.15 |
0.30-0.60 |
0.03 |
0.03 |
0.50MAX |
1.90-2.60 |
0.87-1.13 |
|
* Ni {{0}}.40 maximaal; V 0.18-0.25; Cb 0.06-0.10; N 0.03-0.07; Al 0,04 maximaal |
|||||||
Mechanische eigenschappen van ASTM A199:
|
Staalkwaliteit |
Treksterkte (Mpa) |
Opbrengststerkte (Mpa) |
Verlenging (%) |
Hardheid HRB MAX |
|
ASTM A199 T4 |
415MIN |
170MIN |
30/22 |
85 HRB MAX |
|
ASTM A199 T5 |
415MIN |
170MIN |
30/22 |
85 HRB MAX |
|
ASTM A199 T9 |
415MIN |
170MIN |
30/22 |
85 HRB MAX |
|
ASTM A199 T11 |
415MIN |
170MIN |
30/22 |
85 HRB MAX |
|
ASTM A199 T22 |
415MIN |
170MIN |
30/22 |
85 HRB MAX |